Dental material Enamel Plus HRi (Enamel Plus)

Enamel Plus HRi is a unique dental material for the restoration of teeth of varying complexity, created by Italian developers.

Composite has a low viscosity and a high level of elasticity.

These qualities allow physicians-restorers to produce constructions that are almost identical to natural ones.

Features and distinctive qualities of the composite

Enamel Plus HRi is a light-curing microhybrid material. The increased viscosity of the composite allows dentists to efficiently carry out restoration work on central and chewing teeth.

This operation is facilitated by the density of Enamel. It is the same as original dental coatings. High quality, combined with an affordable technological process, leads to a decrease in the amount of time spent on the restoration procedure.

Tooth enamel and the composite must match. The material cannot look less transparent than the natural layer - according to this parameter, there must be complete external consistency. The similarity of the coefficient characterizing the degree of refraction of light is required. Certain levels of indicators such as illumination, brightness and transparency make the restored tooth natural and healthy.

Dentines in a wide variety of shades are saturated and have a high level of light transmission. There are other qualities of the Enamel material that make it almost indistinguishable from the original. All of them meet the requirements for the latest generation of composites. These include:

• high calibration;
• increased level of fluorescence;
• necessary transparency (opacity).

Dental material Enamel is available in the following colors:

• light (up to the maximum level) and bleached;
• universal;
• dark.

Composite of the last shade, as a rule, is used for complex restorative operations. Dentists actively use this type of material when working in the deep parts of the oral cavity or in the cervical area.

Benefits: functional and technological

Functional advantages of the Enamel Plus HRi dental material:

1. Anatomical restoration. Simplified, which manifests itself in a similar density of natural and replacing tooth enamel.
2. The application technology is easy to use. The number of color shades has been reduced.
3. The quality is high. Lead time is short.
4. The syringe is a new design. The design is simple, the use of consumables is in line with treatment standards. Convenient ergonomics of the medical instrument. The cap is long, without touching the material.
5. Convenience for the attending physician. Composite allows you to do restoration (including indirect method) of the tooth at a high aesthetic level.

Technological advantages:

1. High quality parameters when grinding. Achieved due to the strength of the coating.
2. The physical parameters of the material allow the creation of the highest quality restorations.
3. Enamel plus HRi enamel creates the effect of shades such as amber and blue.
4. The restoration margins are invisible. No special technique is required for their preparation - without the so-called "glass effect", which degrades the quality of the result.
5. The presence of very light dentins.
6. Dentines - are identical to natural ones.

Enamel material types

The composite is used in the following colors:

1. Light (up to the maximum level) and bleached (UD0, UD0.5, UD1).
2. Universal (UD2 (A2), UD3 (A3), UD 3.5 (A 3.5), UD4 (A4)).
3. Dark (UD5, UD6).

When restoring the coating, in the form stains and stripes applied ultra-white composite. It simulates demineralized zones. It is used when processing white (high intensity) surfaces located in the following areas of the oral cavity:

• cervical;
• cutting;
• central (middle) third.

In this line of colors, there are the following types of shades:

• IM (opaque white) - deep and soft;
• IW: opaque white - cold;
• IWS: white - active, dazzling.

Universal enamels consist of the following types of brightness:

1. Low (UE1). Apply in a thin layer (amber opalescence). Adjusting the thickness leads to an increase in brightness.
2. Medium (UE2).
3. High (UE3). Suitable for bleached teeth or ultra-white.

Opalescent coatings: OBN (blue) and OA (amber) enamels create natural opalescence. Transparency 30% up to 0.8 mm.

Instructions for use

Direct way

Initially, the surface of the processed tooth is prepared. For this, a paste without content is used. fluorine. Shades are selected. The card is filled with color options. The chewing teeth are processed without bevel, the front teeth are beveled.

The next stage is etching with phosphoric acid (35-38%). Time for:

• enamels - 35 sec .;
• dentine (vital) - 15 sec .;
• dentine (non-vital) - 120 sec.

Then the surface is washed and dried with a stream of air. If saliva gets on the coating, repeat the procedure - rinsing, drying, re-etching.

The next stage of the process involves covering the cleaned area of ​​enamel and dentin with an adhesive material. Then polymerization, which takes about 40 seconds.

An alternative to this technology is the use of bonding. Self-etching technique.

The stage of work with the Enamel Plus HRi material begins with filling the syringe or “tips” with the required substance, which is recommended to be heated to 39 ° C in thermostatic equipment ENA HEAt. The application of the composite should be done with a brush (so that there are no porous manifestations), small layers.

Final curing takes place after the restoration of the tooth surface is fully aligned or before the last polymerization. It is suggested to use Air Block - a liquid substance containing glycerin. Final polymerization - 3 min. Increasing the procedure time requires the following manipulations:

• use as protection for opaque foil;
• using the palette in color.

The use of abrasive discs is not recommended. They destroy the surface. Should be brushed with diamond brushes and diamond paste. The final shine is best achieved with the Enamel Plus SHINY System.

Indirect

Composite material Enamel Plus is used in the manufacture of:

• surfaces crowns;
• veneers;
• tabs (including cladding).

Stages:

1. Dissection. The procedure is done without undercuts. It is used for restoration work in relation to the chewing tooth sections. It is recommended to use an abrasive tool when processing the inner edges. It is desirable that the layer of material is higher than 1.5 mm.
2. An impression is taken. Enamel Plus temp is used. Fixation is performed on a material that does not contain eugenol.
3. Cuvette (the procedure is performed in a laboratory setting) to be completed silicone hard consistency. Further, it shrinks.
4. Excess material is removed, and the model is covered with a compound for insulation. When making inlays, first of all, the outer walls are lined up, and then the occlusal surface. If necessary, paints of the Enamel Plus composite property are used. The layer thickness must be less than 2 mm. The exposure time takes approximately 40 seconds. The final procedure for this operation lasts no more than 11 minutes - if it is carried out using high power device such as LaborluxL, and 30 minutes with Lampadaplust (86 W).
5. The last stage of the process involves surface grinding and polishing. Then it is washed and dried.
6. Further, the temporary structure is removed. Area in place preparation cleared.
7. The restoration is being tried on. In case of inconsistencies, correction is carried out.
8. Then another polymerization is carried out, repeated cleaning and pickling.
9. It is applied without curing ENA BOND.
10. Sandblasting the interior of the restoration.
11. The Enamel Plus HRi heats up in the thermostat. Application of the substance.
12. After the restoration is installed, it is compressed.
13. Excess material is removed.
14. Polymerization is carried out on each side of the tooth for 80 seconds.
15. The final stage is checking, grinding, polishing.

The prognosis of the result when using Enamel plus HRi is due to the following factors. The material has an undeniable advantage over other composites. When restoring with this substance, the doctor is practically not limited by its capabilities (quality, the duration of wearing the structure, aesthetic properties, etc.) - which cannot be said about analogues composite.

Manufacturer, release form, price

Manufacturer - Micerium S.p. A. (Italy).

Product release form - syringe with material, volume - 2.5 or 5 g.

The price of the material Enamel Plus is 5900 rubles.